cw 617 n, dtd 627, modified forging brass, brass modified forging, forging brass rods, brass extrusion rods, Brass hollow rods, brass hollow sections, brass extruded rods, brass extrusion sections, brass extrusion profiles, brass knurling rods, brass ingots, brass billets, Brass Extrusion Coil Wires, brass extrusions, brass profiles, brass sections, brass flats

CW617N is the most frequently used alloy for Hot Stampings. It has an excellent capacity for Hot Forming along with good machinability properties.

Equivalent Specifications:

CZ122	BS218
CuZn40Pb2

Nominal Composition:

Copper	57 to 59%
Lead	1.6 to 2.5%
Iron	0.30% Max
Zinc	Balance

Key Features:

» Machinability rating of 100%.
» Excellent capacity for hot forming.
» Good Corrosion resistance.
» Excellent suitability for Brazing and Soldering.

Yield Stress	150 MPa Min.
Tensile Strength	380 MPa Min.
Hardness Brinell	90 to 160 HB
Elongation	18 Min.