Manganese Bronze comes from a family of High strength copper based alloys which includes Manganese as an alloying agent with additions of Iron, Aluminium, Zinc, Lead and sometimes Nickle or Silicon. It has exceptionally high strength as compared to normal brass and therefore commonly known as High Tensile Brass, High Tensile Manganese Bronze, High Strength Brass or Manganese Aluminium Bronze. Like Aluminium Bronzes, High Tensile brasses offers a variety of properties in the form of higher strength levels, non-corrosive properties, improved hardness, yield strength and tensile strength. Some of the High Tensile Brasses are known to have excellent hot forming properties and can be used in environments where soldering, welding or brazing is required.
C6782 Manganese Bronze alloy has good corrosion resistance properties. Additions of Manganese in the alloy makes it highly valuable for its excellent performance and reliable operations.
| ELEMENT | Copper | Iron | Manganese | Zinc | Lead | Aluminium |
|---|---|---|---|---|---|---|
| Min (%) | 56.00 | 0.10 | 0.50 | Balance | - | 0.20 |
| Max (%) | 60.50 | 1.00 | 0.25 | 0.50 | 2.00 |
Adinath produces C-66800, C-67300, C-67400, C-67410, C-67420, C-67500, C-67600, C-6783, C-86200, C-86300, C-86400, C-86500, CW710R, CW713R, CW721R, CW722R, CW723R, CZ114, CZ115, CZ135, CZ136, IS:320HT-I, IS:320HT-II, 6912 FHTB-I, 6912 FHTB-II, High Tensile Brass alloy in the form of Extruded Rods in different shapes & sizes.
From: Dia 10 mm up to 120 mm.
From: A/F 10 mm up to 100 mm.
From: A/F 10 mm up to 90 mm.
From: A/F 10 x 12 mm up to 100 x 50 mm.
Outer Diameter: In Round, Hex & Square.
From: 30 mm up to 120 mm.
Inner Diameter (Round):
From: 20 mm up to 80 mm.
As per Customers' Drawing.
Length: Up to 4 Meters.
Delivery Condition: As Extruded or Cold Drawn.
Straight Knurling & Cross Knurling will be available upon shape & size Feasibility of Brass Rod
AEPL's Quality Management System ensures documented process controls from start to finish. Material identification and inspection are carried out in all stages of production.
Chemical check by Handheld analyzers.
Pyrometers and Optical Emission Spectrometer.
Identification by Punching Heat Codes.
Tag allocation by Heat Number/Order codes as it moves down the production line.
Mechanical Testing - Tensile Strength, Elongation and Hardness.
Handling, Processing and Packaging Procedures to ensure delivery in prime condition.
All bars manufactured at AEPL are supplied with full certifications helping us to deliver the exact specification demanded by our specific customer base.
AEPL manufactures and supplies Copper Alloys Extruded Bars to Domestic as well as International Markets. Our customer base has a key advantage since our Foundries, Laboratories, Extrusion Mill, Shell Mouldings and CNC Machine shop are all located on a single site, which eliminates waste and allows excellent quality control at each stage. Our ability to reclaim swarf and machined chips allows us to offer competitive pricing for the parts that we either extrude or cast. For further details, please visit the below link.
| Range (mm) | UTS Min (Mpa) | PS Min (Mpa) | Elongation Min (%) | Hardness (HRB) |
|---|---|---|---|---|
| 4 to 50 Incl. | 420 | 240 | 15 | - |
| Range (mm) | UTS Min (Mpa) | PS Min (Mpa) | Elongation Min (%) | Hardness (HRB) |
|---|---|---|---|---|
| 4 to 50 Incl. | 420 | 240 | 15 | - |
| Range (mm) | UTS Min (Mpa) | PS Min (Mpa) | Elongation Min (%) | Hardness (HRB) |
|---|---|---|---|---|
| 4 to 50 Incl. | 420 | 240 | 15 | - |
| Range (mm) | UTS Min (Mpa) | PS Min (Mpa) | Elongation Min (%) | Hardness (HRB) | |
|---|---|---|---|---|---|
| Thickness | 4 to 50 Incl. | 420 | 240 | 15 | - |
| soldering | brazing | machinability rating |
|---|---|---|
| EXCELLENT | FAIR | 30 |
| product category | DESCRIPTION |
|---|---|
INDUSTRIAL: |
Gate Valve Stems, Valve Balls, Welding Rod. |